Grade No.:PECD2506
Description:PECD2506 is a permanent conductive special material
modified with conductive carbon black as a conductive additive.
The base material is HDPE resin.
The surface resistivity of this product is stable and it is suitable
for application fields that require excellent conductive performance
Application:such as conductive and anti-static films, sheets, injection molding, etc.
Feature:Reasonable price,Surface resistivity 10-4Ω/sq,stable quality
Advantage:stable quality，stable better than conductive masterbatch,customize available,Surface resistivity 10-4Ω/sq
Free samples:about 2kgs
Sample lead time:about 0-3days
MOQ:About 100kgs/bag EXW price
Production lead time:about 0-10days depends on the stock and production plans.
Packaging: 25kgs/bag,about 1ton/pallet,about 18-20tons/20GP with pallets
And 28tons/40QH with pallets,about 28tons/20GP without pallets
Test Item | Method | Unit | Value |
Appearance | By eyes | - | Black particles |
Melt index (200℃,5kg) | ASTM D1238 | g/10min | 12 |
Density | ASTM D792 | g/cm3 | 1.05 |
Tensile strength | ASTM D638 | kgf/cm2 | 240 |
Tensile elongation | ASTM D638 | % | 9.0 |
Bending strength | ASTM D790 | kgf/cm2 | 370 |
Bending modulus | ASTM D790 | kgf/cm2 | 9200 |
Izod notched impact strength (3.2mm) | ASTM D256 | kgf-cm/cm | 5.5 |
Heat distortion temperature (0.45MPa) | ASTM D648 | ℃ | - |
Flame retardant grade (3.2mm) | UL 94 | - | - |
Surface resistivity | ASTM D257 | Ω/sq | 10-4 |
Shrinkage rate | ASTM D955 | % | 2.20 |
Pre-drying conditions | Extrusion temperature | |||
Die head/die section | The front part | Middle part | The rear part | |
80℃,4-5 Hr | 200-210℃ | 190-200℃ | 180-190℃ | Room temperature |